Firing Athenian black and red figure vases


Jan van der Crabben
by Trustees of the British Museum
published on 02 August 2011
Send to Google Classroom:

A distinctive red and black colour scheme characterises most of the painted pottery of sixth- and fifth-century Athens. The colours result from the skilful exploitation of the high iron content of Athenian clay by an ingenious process of differential firing. The black areas of a black or red-figured pot were coated in a fine solution of the same clay that was used for the body of the vase. Before the vase was placed in the kiln, it would have been orange-red in colour, with the coated areas slightly deeper in tone.

Black-figured amphora (wine-jar) signed by Exekias as potter and attributed to him as painter
Black-figured amphora (wine-jar) signed by Exekias as potter and attributed to him as painter
by Trustees of the British Museum (Copyright)

Once the kiln had been loaded, the a three-stage firing took place. In the first, oxidising, phase plenty of air was allowed into the kiln, and the temperature was gradually made to rise to around 800º C. At this point, the vase turned a bright orange-red, as the oxygen in the atmosphere combined with the iron in the clay to produce (red) ferric oxide.

Remove Ads


When the potter judged that the required temperature had been reached, he stopped up the air vents and perhaps introduced damp material in the form of green wood or even bowls of water. This produced a reducing (oxygen-poor) atmosphere in the kiln and the red ferric oxide was converted to (black) ferrous oxide, so that the entire pot turned black. The temperature in the kiln continued to rise to around 945º C. The intense heat caused the fine particles of the clay of the coated areas of the pot to 'sinter', that is, to fuse together to form a hard, smooth, almost glassy surface.

In the third and final stage, the temperature was allowed to drop, and at about 900º C the ventilation holes were opened up, oxygen returned to the atmosphere of the kiln, and the ferrous oxide of the uncoated areas converted back to ferric oxide, so that as the kiln cooled down these parts turned orange-red again. The sealed surface of the sintered areas was impervious to the presence of the oxygen and so remained black.

Remove Ads


Editorial Review This article has been reviewed for accuracy, reliability and adherence to academic standards prior to publication.
Remove Ads




We want people all over the world to learn about history. Help us and translate this article into another language!

Support Our
Non-Profit Organization

World History Encyclopedia is a non-profit organization. For only $5 per month you can become a member and support our mission to engage people with cultural heritage and to improve history education worldwide.

Become a Member  

Recommended Books

Sorry, we haven't been able to find any books on the subject.

Cite This Work

APA Style

Museum, T. O. T. B. (2011, August 02). Firing Athenian black and red figure vases. World History Encyclopedia. Retrieved from

Chicago Style

Museum, Trustees O. T. B. "Firing Athenian black and red figure vases." World History Encyclopedia. Last modified August 02, 2011.

MLA Style

Museum, Trustees O. T. B. "Firing Athenian black and red figure vases." World History Encyclopedia. World History Encyclopedia, 02 Aug 2011. Web. 08 Mar 2021.

Remove Ads


Powered by Mailchimp


Our latest articles delivered to your inbox, once a week:

Are you a...?

Remove Ads


Partner Promotion

Remove Ads


Our Videos

You can also follow us on Youtube!